作者(2019)在《Prediction of properties distribution of 7B50 alloy thick plates after quenching and aging by quench factor analysis method》一文中研究指出:In the present work,continuous cooling curves were accurately measured by the modified Jominy specimen of 7B50 alloy during water-spray quenching tests.Besides,the time-temperature-properties(TTP) curves of this alloy were obtained during isothermal treatments.Based on the accurate cooling curves and TTP curves,the hardness distribution along the thickness direction of 7B50 alloy thick plates was predicted by quench factor analysis method.It is found that the quench sensitive temperature range of 7B50 alloy is 240-410℃,the nose temperature is 335℃,and the incubation period at the nose temperature is about 0.87 s.When 7B50 alloy was isothermal treated at 180-400℃ after solid solution treatment(470℃ for 1 h followed by 483℃ for 2 h),the exponent(n) in the Johnson-Mehl-Avrami equation is close to 1 until transformed fraction of new precipitates is up to 60%,indicating that new precipitates first grow into rodlike shape and then coarsen or thicken.When the distance is less than 65 mm from the spray quenching surface of the modified Jominy specimen,the deviation between the predicted and measured hardness is less than 2.7%,confirming the quench factor analysis method as the feasible way to predict the hardness distribution along the thickness direction of 7B50 alloy thick plates.When the distance from the spray quenching surface is 25 mm,the average cooling rate in quench sensitive temperature range is 9.93 ℃·s-1,while the quench factor(τ) is 9.89 and the corresponding predicted hardness is HV 185.1 equivalent to 97.3% of the maximum measured hardness of 7B50 alloy in T6 temper.

Abstract

In the present work,continuous cooling curves were accurately measured by the modified Jominy specimen of 7B50 alloy during water-spray quenching tests.Besides,the time-temperature-properties(TTP) curves of this alloy were obtained during isothermal treatments.Based on the accurate cooling curves and TTP curves,the hardness distribution along the thickness direction of 7B50 alloy thick plates was predicted by quench factor analysis method.It is found that the quench sensitive temperature range of 7B50 alloy is 240-410℃,the nose temperature is 335℃,and the incubation period at the nose temperature is about 0.87 s.When 7B50 alloy was isothermal treated at 180-400℃ after solid solution treatment(470℃ for 1 h followed by 483℃ for 2 h),the exponent(n) in the Johnson-Mehl-Avrami equation is close to 1 until transformed fraction of new precipitates is up to 60%,indicating that new precipitates first grow into rodlike shape and then coarsen or thicken.When the distance is less than 65 mm from the spray quenching surface of the modified Jominy specimen,the deviation between the predicted and measured hardness is less than 2.7%,confirming the quench factor analysis method as the feasible way to predict the hardness distribution along the thickness direction of 7B50 alloy thick plates.When the distance from the spray quenching surface is 25 mm,the average cooling rate in quench sensitive temperature range is 9.93 ℃·s-1,while the quench factor(τ) is 9.89 and the corresponding predicted hardness is HV 185.1 equivalent to 97.3% of the maximum measured hardness of 7B50 alloy in T6 temper.

论文参考文献

  • [1].Influences of processing routine on mechanical properties and structures of 7075 aluminum alloy thick-plates[J]. 林高用,张辉,张行健,韩冬峰,张颖,彭大暑.  Transactions of Nonferrous Metals Society of China.2003(04)
  • [2].Through-thickness inhomogeneity of localized corrosion in 7050-T7451 Al alloy thick plate[J]. 丰雷,潘清林,韦莉莉,黄志其,刘志铭.  Journal of Central South University.2015(07)
  • [3].Optimization design of wide face water slots for medium-thick slab casting mold[J]. Xue-lin Yin,Li Wu,Jun-jia Zhang,Hui-jun Kang,Zong-ning Chen,Jin-song Chen,Zhi-qiang Cao,Ting-ju Li,Tong-min Wang.  China Foundry.2016(05)
  • [4].Surface modification of (Tb0.3Dy0.7)Fe1.95 alloy by ion nitriding process[J]. 李扩社,李红卫,严辉,于敦波,王丰瀛,张世荣,张国成.  Journal of Rare Earths.2009(02)
  • [5].Variations of properties across plate thickness for Al alloy 7010[J]. M.Salazar-Guapuriche,Y.Y.Zhao,A.Pitman,A.Greene.  Transactions of Nonferrous Metals Society of China.2005(06)
  • [6].Ageing behavior of an Al-Zn-Mg-Cu alloy pre-stretched thick plate[J]. Zhihui Li, Baiqing Xiong, Yongan Zhang, Baohong Zhu, Feng Wang, and Hongwei Liu State Key Laboratory for Fabrication and Processing of Non-ferrous Metals, General Research Institute for Non-ferrous Metals, Beijing 100088, China.  Journal of University of Science and Technology Beijing.2007(03)
  • [7].Effects of aging parameters on hardness and electrical conductivity of Cu-Cr-Sn-Zn alloy by artificial neural network[J]. 苏娟华,贾淑果,任凤章.  Journal of Central South University of Technology.2010(04)
  • [8].Characterization of the microstructure and hardness of the HAZ in a 800MPa grade RPC steel[J]. 马成勇,田志凌,杜则裕,彭云,张晓牧,何长红.  China Welding.2005(01)
  • [9].Microstructure and hardness of binary Cr-Ta alloys[J]. 张兆森,贺跃辉,黄伯云,彭超群.  Transactions of Nonferrous Metals Society of China.2002(02)
  • [10].Effect of thermal exposure on precipitation behavior and hardness of alloy 718[J]. GENG Lin(耿 林) 1, ZHENG Zhen zhu(郑镇洙) 1, Na Yong Sang 2, Park Nho Kwang 2 1. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, P.R.China 2. Korea Institute of Machinery and Materials, 66 Sangnamd.  Transactions of Nonferrous Metals Society of China.2000(03)
  • 论文详细介绍

    论文作者分别是来自Rare Metals的,发表于刊物Rare Metals2019年11期论文,是一篇关于,Rare Metals2019年11期论文的文章。本文可供学术参考使用,各位学者可以免费参考阅读下载,文章观点不代表本站观点,资料来自Rare Metals2019年11期论文网站,若本站收录的文献无意侵犯了您的著作版权,请联系我们删除。

    标签:;  

    :Prediction of properties distribution of 7B50 alloy thick plates after quenching and aging by quench factor analysis method论文
    下载Doc文档

    猜你喜欢